PE water pipe fittings should be stored away from fire sources and insulated areas.

Detailed 1PE water supply pipe construction without shaft right, no network oxide skin, welding cooling time is not enough to cause electrofusion welding defects, these defects can not be exposed in a short period of time, in addition, there is no effective means of detection, the road surface will settle. Pressure regulating cabinet of the foundation settlement of the internal stress will make defects exposed, the occurrence of air leakage, this leakage is very harmful, easy to cause accidents.PE homogeneous siphon fittings factory we together to observe the PE electrofusion filament of the specific construction environment of the abnormal causes.

(1) PE water supply pipe of the internal resistance line overflow; bottom is not inserted into the bottom; PE water supply pipe joints

(2) Cavity; and resistance line sparse; local high temperature PE material gasification after cooling formation;

(3) a resistance wire overflow; a resistance wire root smaller cavity in a ring through the formation of air flow path;

(4) from the red marking line of the installation is problematic, PE homogeneous siphon pipe fittings wholesale shaft alignment; there are Ming's company is specializing in the production of PE water supply pipe, electrically welded joints manufacturers, the company's advanced production equipment is the cooling and calibration: pipe and pipe heat butt joints, it must be strictly adhered to the necessary holding and cooling time. During the holding time, the weld seam just welded can be modified, but not allowed to rotate.PE homogeneous siphon pipe fittings supply 2, welding: the temperature of the hot melt machine reaches 260 ° C, the implementation of the hot melt machine to maintain the stability of the hot melt machine shaking. Pipes and pipe fittings to maintain the level with the hot melt melting mould with, at the same time inserted, pipe fittings at one end little by little to enhance the propulsion, connecting pipes and pipes. Keeping the front end of the low-speed, fixed-speed, and synchronised da-type, the inner edge is flipped at the end of the pipe, and at this time, the hot melt melter pulls out the pipe and the tube along the horizontal direction at the same time, and inserts them axially without rotating rapidly, and connects the joints.